Woven fibre cloth + flame-retardant acrylic adhesive + release paper. Layer and interlayer insulation in transformers, motors, high-frequency and microwave-oven transformers and capacitors; harness wrapping and bundling; fixing of deflection-coil ferrites, ceramic heaters and quartz tubes.
Values in this family are measured in-house on the instruments named on each datasheet — thickness gauge, 180° peel tester, holding-power tester, ball-tack tester, dielectric tester and flammability tester. They are our own production-control readings, not third-party test results.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.12 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1000 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.17 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Opacity | ≥99.5% | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1500 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1500 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.22 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.12 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1000 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.21 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1500 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.12 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Opacity | ≥99.5% | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1000 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Opacity | ≥99.5% | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.12 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 900 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥5 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
Issued as two TDS variants — standard and non-hand-tearable — with identical measured values.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.16 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 1300 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Not flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 900 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 600 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant — UL Recognized Component (see note) | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
The TDS for this model prints UL file E544340, but the UL certificate we hold lists type Z1V020 only. We do not state UL Recognized Component status for this model until the UL addendum listing the additional type designations is in hand.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1240 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 900 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 800 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
| Property | Value | Method |
|---|---|---|
| Colour | Black | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 600 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant — UL Recognized Component (see note) | in-house instrument |
| UL Recognized Component | UL file E544340 | ANSI/CAN/UL 510A |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
An earlier TDS revision (last modified 2025-03-27) stated ≥800 gf/inch and carried "V-0" in its header. The figures here come from the current revision (2026-09-08), which states ≥600 gf/inch and no longer carries the V-0 wording. Confirm the revision that applies to your order.
| Property | Value | Method |
|---|---|---|
| Colour | White | in-house instrument |
| Total thickness | 0.20 ± 0.01 mm | in-house instrument |
| Master-roll width | 1270 mm (master roll; slit to spec) | in-house instrument |
| Peel adhesion, 180° | ≥ 600 gf/inch (180°) | in-house instrument |
| Holding power | ≥ 48 h | in-house instrument |
| Service temperature | 80 °C | in-house instrument |
| Ball tack | ≥8 (ball no.) | in-house instrument |
| Dielectric strength | 1.5 kV | in-house instrument |
| Flame behaviour | Flame retardant — UL Recognized Component (see note) | in-house instrument |
LV 312 class: not classified. We do not estimate one from the values above — what a classification needs.
The TDS for this model prints UL file E544340, but the UL certificate we hold lists type Z1V020 only. We do not state UL Recognized Component status for this model until the UL addendum listing the additional type designations is in hand.
The technical data on this page is reproduced from the manufacturer's datasheet for the model named. It is for reference only and is not intended as a basis for product acceptance; for a special application, test and confirm before use.
Best-before 6 months from despatch. Store at 25 °C / 65 % RH in a cool, ventilated place, out of direct sunlight.
Two of our harness grades carry class designations on their own datasheet, with the test standard printed next to each value. The rest of the range does not, and we do not estimate a class from a peel figure or an in-house temperature reading.
| Model | Property | Value on our datasheet | Test standard cited |
|---|---|---|---|
| K8030 | temperature | −40 °C to +105 °C | LV 312 |
| K8030 | noise damping | Class C — 5 to ≤10 dB | LV 312 |
| K8030 | scrape abrasion | Class B — 100–499 cycles | ISO 6722 |
| K8030 | flammability | Class B — self-extinguishing | ISO 3795 |
| K8030 | peel adhesion | ≥ 3 N/cm | EN 1939 |
| K8030 | tensile strength | ≥ 30 N/cm | EN 14410 |
| K8030 | elongation at break | ≥ 20 % | EN 14410 |
| K75100-00 | temperature | −40 °C to +105 °C | declared on the TDS; test standard not printed |
| K75100-00 | noise damping | Class A — ≤2 dB | declared on the TDS; test standard not printed |
| K75100-00 | burn rate | ≤ 100 mm/min | declared on the TDS; test standard not printed |
An LV 312 class is the result of a specified test, not a property you can read off a datasheet. The acetate, nylon and conductive grades below report a 80 °C service temperature measured in-house on our own instruments — that is not an LV 312 temperature class, and we do not print one. Classification is done per tape model, on the construction actually supplied.
Temperature class, scrape abrasion (cited as ISO 6722 on our classified grade, and only meaningful with the mandrel diameter next to it), noise damping in dB, and flammability (cited as ISO 3795). Each is measured separately on the same model — a high temperature class says nothing about abrasion. Peel and tensile on those reports are cited to EN 1939 and EN 14410.
Tell us the model and the class your drawing calls for. We submit the construction for test and send you the report with the model number on it — we do not transfer another grade’s result onto it.
Request a classification & reportEach report covers the sample that was submitted. Where the report names a model number it is model-level; where it names a product category it covers the construction, and we say so rather than attaching it to a single model.
The standard electronic-insulation cloth — heat-resistant, paint-absorbing, easy-tear.
Explore
Compliance is king — UL 510A Recognized Component, UL 94 V-0 grades, zero-halogen options.
Explore
Opaque matte-black blackout tape for displays, optics, stage & photo — opacity confirmed per model.
ExploreMaster rolls are slit to your width, and we build to a drawing. Send the model and the dimension you need.
Request a quote & samples